PPS 1200L1 CELANESE USA
FORTRON®
Electrical applications,Automotive Applications
Elongated elongation rate,high viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 200 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 93 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| dielectric constant | 10kHz | ASTM D150 | 3.00 |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.0 % |
| 断裂 | ISO 527-2/1A/50 | 15 % | |
| Tensile modulus | ISO 527-2/1A/1 | 4000 Mpa | |
| bending strength | 23°C | ISO 178 | 141 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4100 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/50 | 88.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| Viscosity | 内部方法 | 430 Pa·s | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/1200L1 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 275 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 4.2E-05 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 90.0 °C |