AS(SAN) KIBISAN® PN-106 L150 FG CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/KIBISAN® PN-106 L150 FG |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 2.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/KIBISAN® PN-106 L150 FG |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2600 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 4.0 % |
| bending strength | ISO 178 | 89.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 MPa |
| 断裂 | ISO 527-2/50 | 65.0 MPa |
| flammability | Test Condition | Test Method | CHI MEI CORPORATION/KIBISAN® PN-106 L150 FG |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/KIBISAN® PN-106 L150 FG |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 32.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.06 g/cm³ |
| Shrinkage rate | ISO 294-4 | 0.20to0.70 % |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/KIBISAN® PN-106 L150 FG |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 104 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 99.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 88.0 °C | |
| vicat | -- | ISO 306/B50 | 101 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.6E-5to3.8E-5 cm/cm/°C |