ABS LG ABS HI121H LG Chem Ltd.
--
Electrical and electronic application fields
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 230 J/m |
| hardness | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 110 |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >10 % |
| bending strength | 3.20mm | ASTM D790 | 76.5 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2550 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 49.0 MPa |
| flammability | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40to0.70 % |
| density | ASTM D792 | 1.04to1.07 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./LG ABS HI121H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 86.0 °C |
| vicat | ASTM D15254 | 94.0 °C |