Mechanical properties	Test Condition	Test Method	SABIC SAUDI/30YM243
tensile strength	屈服,80℃, 注塑	ISO 527-2/1B	70.0 Mpa
Dart impact	23℃	ISO 6603-2	58.0 J/cm
Tensile modulus	120℃, 注塑	ISO 527-2/1B	3500 Mpa
Charpy Notched Impact Strength	23℃, 注塑	ISO 179/1eU	52 kJ/m²
tensile strength	屈服,23℃, 注塑	ISO 527-2/1B	110 Mpa
Tensile strain	断裂,23℃, 注塑	ISO 527-2/1B	2.3 %
Flexural modulus	23℃, 注塑	ISO 178	5900 Mpa
Charpy Notched Impact Strength	-30℃, 注塑	ISO 179/1eU	36 kJ/m²
bending strength	23℃, 注塑	ISO 178	147 Mpa
bending strength		80℃, 注塑	ISO 178	86.0 Mpa
Charpy Notched Impact Strength	23℃, 注塑	ISO 179/1eA	19 kJ/m²
Tensile modulus	23℃, 注塑	ISO 527-2/1B	6650 Mpa
Tensile modulus		80℃, 注塑	ISO 527-2/1B	4600 Mpa
Charpy Notched Impact Strength	-30℃, 注塑	ISO 179/1eA	25 kJ/m²
Flexural modulus	80℃, 注塑	ISO 178	4200 Mpa
tensile strength	屈服,120℃, 注塑	ISO 527-2/1B	51.0 Mpa

Thermal performance	Test Condition	Test Method	SABIC SAUDI/30YM243
Linear coefficient of thermal expansion	23℃-80°C	ASTM D696	0.000041 cm/cm/℃
Linear coefficient of thermal expansion		-30℃-30℃	ASTM D696	0.000051 cm/cm/℃
Heat distortion temperature	1.8 MPa, 未退火，HDT	ISO 75-2/A	156 °C