HMW-HDPE TOTAL Polyethylene HDPE 2287 TOTAL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 2287 |
|---|---|---|---|
| Elmendorf tear strength | 20µm,BlownFilm，MD | ASTM D1922 | 24 g |
| Water Vapor Transmission Rate | ASTME96 | 12 g/m²/24hr | |
| tensile strength | Yield,20µm,BlownFilm | ASTM D882A | 34.5 MPa |
| Tensile strain | Break,20µm,BlownFilm | ASTM D882A | 300to500 % |
| film thickness | 20 µm | ||
| Elmendorf tear strength | 20µm,BlownFilm，TD | ASTM D1922 | 120 g |
| tensile strength | Break,20µm,BlownFilm | ASTM D882A | 67.6 MPa |
| Secant modulus | 20µm,BlownFilm | ASTM D882A | 910 MPa |
| Dart impact | 20µm,吹塑薄膜 | ASTM D1709A | 350 g |
| Tensile strain | Break,20µm,BlownFilm，MD | ASTM D882A | 300to500 % |
| physical property | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 2287 |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 11 g/10min |
| density | ASTM D792 | 0.950 g/cm³ | |
| melt mass-flow rate | 190°C/5.0kg | ASTM D1238 | 0.32 g/10min |
| 190°C/2.16kg | ASTM D1238 | 0.080 g/10min |
| Thermal performance | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 2287 |
|---|---|---|---|
| melting temperature | ASTM D3417 | 127 °C |