Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPU A92P4851 HUNTSMAN GERMANY
IROGRAN®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | HUNTSMAN GERMANY/A92P4851 |
|---|---|---|---|
| Shore hardness | 邵氏D,注塑 | ISO 868 | 42 |
| 邵氏A,注塑 | ASTM D2240 | 93 | |
| 邵氏D,注塑 | ASTM D2240 | 42 | |
| 邵氏A,注塑 | ISO 868 | 93 |
| Mechanical properties | Test Condition | Test Method | HUNTSMAN GERMANY/A92P4851 |
|---|---|---|---|
| wear resistance | ISO 4649 | 35 mm³ |
| physical property | Test Condition | Test Method | HUNTSMAN GERMANY/A92P4851 |
|---|---|---|---|
| Shrinkage rate | 0.50 % | ||
| MD | ASTM D955 | 0.10 % | |
| Melt volume flow rate | 190°C/21.6kg | 55.0 cm3/10min |
| elastomer | Test Condition | Test Method | HUNTSMAN GERMANY/A92P4851 |
|---|---|---|---|
| tensile strength | 100%应变 | ASTM D412 | 10.0 Mpa |
| elongation | 断裂 | ASTM D412 | 630 % |
| compression set | 23°C,24hr | ISO 815 | 25 % |
| 70°C,24hr | ASTM D395 | 45 % | |
| tensile strength | 300%应变 | DIN 53504 | 16.0 Mpa |
| compression set | 23°C,24hr | ASTM D395 | 25 % |
| 巴肖氏弹性 | ISO 815 | 33 % | |
| tensile strength | 300%应变 | ASTM D412 | 14.5 Mpa |
| compression set | 70°C,24hr | ISO 815 | 45 % |
| tensile strength | 断裂 | DIN 53504 | 40.0 Mpa |
| tear strength | ISO 34-1 | 75 kN/m | |
| elongation | 断裂 | DIN 53504 | 600 % |
| tensile strength | 断裂 | ASTM D412 | 35.9 Mpa |
| tear strength | ASTM D624 | 112 kN/m | |
| tensile strength | 100%应变 | DIN 53504 | 10.0 Mpa |
| Thermal performance | Test Condition | Test Method | HUNTSMAN GERMANY/A92P4851 |
|---|---|---|---|
| melting temperature | 160to171 °C |