PC MB2112 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and electrical、Fitness equipment
Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2100 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 93 % | |
| bending strength | ISO 178 | 86.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| tensile strength | 屈服 | ISO 527-2 | 59.0 Mpa |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| characteristic | 瓷白防火V-0 | ||
| purpose | 电工电子器材 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.60-0.80 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.60 cm3/10min |
| Shrinkage rate | 吸水率(饱和,23°C) | 0.20 % | |
| MD:3.20mm | 0.60-0.80 % | ||
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB2112 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 138 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 113 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |