PPO WCA871-111 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Wire insulation applicati
Low Specific Gravity、Low water absorption、Non enhanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
Shore hardness邵氏A,30秒ASTM D224087
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
Flexural modulus100mmSpanASTM D790100 Mpa
tensile strength 断裂CCP METHOD30.0 Mpa
elongation断裂2ASTM D638140 %
Flexural modulusISO 178100 Mpa
elongation断裂,136°C3CCP METHOD200 %
tensile strength 断裂2ASTM D63818.0 Mpa
elongation断裂CCP METHOD280 %
Tensile strain断裂ISO 527-2/50130 %
tensile strength 断裂ISO 527-2/5018.0 Mpa
断裂,136°C3CCP METHOD27.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
Volume resistivityASTM D2572.4E+16 ohms·cm
relative permittivity1MHzIEC 602502.60
dielectric strength1.50mm,inOilIEC 60243-128 KV/mm
Dissipation Factor1MHzIEC 602502.8E-03
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
Smoke densityNon-Flame,0.5mmplaque,Ds,maxASTME66267
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13825 °C
Smoke densityFlame,0.5mmplaque,Ds,maxASTME662140
Limiting Oxygen IndexISO 4589-228 %
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
melt mass-flow rate250°C/5.0kgASTM D123815 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCA871-111
UL temperature ratingCCP METHOD105 °C
brittle temperatureASTM D746-40.0 °C
Heat distortion temperature121°CCCP METHOD20 %