Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS POLYREX® PH-888G CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-888G |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 93 MPa |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-888G |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 1400 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.00 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 28 MPa |
| elongation at break | 23°C | ISO 527-2 | 50 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| bending strength | 23°C | ISO 178 | 45 MPa |
| Flame retardant performance | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-888G |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-888G |
|---|---|---|---|
| density | ISO 1183 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/POLYREX® PH-888G |
|---|---|---|---|
| vicat | ISO 306/A50 | 100 °C | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 79 °C |
| vicat | ISO 306/B50 | 91 °C | |
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/A | 95 °C |