Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC AC3900 FCFC TAIWAN
TAIRILITE®
Automotive sector,Laptop case,Electrical field,Electronic field
Flame retardant,Thermal stability,enhance,High temperature resistan,high viscosity
UL
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 590 J/m |
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 121 |
| R 级, 23°C | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 104 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2350 Mpa |
| tensile strength | 23°C | ASTM D638 | 60.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.50 - 0.70 % |
| density | 23°C | ISO 1183 | 1.28 g/cm³ |
| Shrinkage rate | 3.20 mm | ISO 2577 | 0.50 - 0.70 % |
| density | -- | ASTM D792 | 1.28 g/cm³ |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 26 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 3.18 mm，HDT | ASTM D648 | 124 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/AC3900 |
|---|---|---|---|
| drying time | 4.0 to 8.0 hr | ||
| Injection Pressure | 4.90 to 7.85 Mpa | ||
| Processing (melt) temperature | 260 to 290 °C | ||
| drying temperature | 120 to 130 °C | ||
| Temperature | 80 to 100 °C |