Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Polyolefin, Unspecified CALP WW672 Lion Idemitsu Composites Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 7.70 kJ/m² |
| hardness | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 94 |
| Mechanical properties | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 35 % |
| tensile strength | ASTM D638 | 28.0 MPa | |
| Flexural modulus | ASTM D790 | 1450 MPa | |
| bending strength | ASTM D790 | 37.0 MPa |
| flammability | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 1.8 % |
| density | ASTM D792 | 0.950 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 35 g/10min | |
| Shrinkage rate | MD:2.00mm | 内部方法 | 1.5 % |
| Thermal performance | Test Condition | Test Method | Lion Idemitsu Composites Co., Ltd./CALP WW672 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 125 °C |
| RTI Imp | UL 746 | 65.0 °C | |
| ball-indentation hardness | 135°C | 内部方法 | 通过 |
| RTI | UL 746 | 65.0 °C | |
| RTI Elec | UL 746 | 65.0 °C |