Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS P2HGV BK901510 INEOS USA
Novodur®
Automotive sector、Application in the automo
heat-resisting、high strength、High rigidity、Filler: Glass fiber reinf、16% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 18 kJ/m² |
| -30°C | ISO179 | 20 kJ/m² |
| hardness | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| ISO2039-1 | 135 Mpa |
| Mechanical properties | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| Bending stress | ISO178 | 101 Mpa | |
| Tensile modulus | ISO527-2 | 5500 Mpa | |
| Flexural modulus | ISO178 | 5400 Mpa | |
| Tensile stress | 屈服,23°C | ISO527-2 | 74.0 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 2.0 % |
| Tensile stress | 断裂,23°C | ISO527-2 | 74.0 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+14 ohms | |
| 100Hz | IEC60250 | 2.90 | |
| CTI | IEC60112 | 575 V | |
| Dissipation Factor | 100Hz | IEC60250 | 5E-03 |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.50mm | IEC60243-1 | 32 KV/mm |
| Dissipation Factor | 1MHz | IEC60250 | 6E-03 |
| 1MHz | IEC60250 | 3.10 |
| physical property | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| Ash Content | 16 % | ||
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 3.00 cm3/10min |
| Shrinkage rate | ISO294-4 | 0.20到0.40 % |
| Thermal performance | Test Condition | Test Method | INEOS USA/P2HGV BK901510 |
|---|---|---|---|
| vicat | ISO306/B50 | 105 °C | |
| Hot deformation temperature 3 | 1.8MPa,退火 | ISO75-2/A | 102 °C |
| 0.45MPa,退火 | ISO75-2/B | 106 °C | |
| MD | ISO11359-1 | 4E-05 cm/cm/°C |