POM FU2025 MITSUBISHI THAILAND
Iupital™
Automotive sector、Electronic and Electrical
wear resistant、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/FU2025 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 19 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/FU2025 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1600 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | >100 % | |
| bending strength | ISO 178 | 48.0 Mpa | |
| Flexural modulus | ISO 178 | 1400 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 12 % |
| tensile strength | 屈服 | ISO 527-2 | 39.0 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI THAILAND/FU2025 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/FU2025 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 5.20 cm3/10min |
| density | ISO 1183 | 1.35 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 6.0 g/10min |
| Shrinkage rate | MD：3.00mm | 1.7 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/FU2025 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 76.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |