PPO PX1112-701 SABIC INNOVATIVE US

NORYL™

Automotive body panels,Automotive sector

Dimensional stability,Low Specific Gravity

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Ball Pressure Test	H 358/30	ISO 2039-1	80.0 Mpa

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	120 °C
Hot deformation temperature		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	105 °C
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K
Vicat softening temperature	--	ISO 306/B120	125 °C
		--	ISO 306/B50	120 °C
		--	ISO 306/A50	130 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Bending modulus		ISO 178	1900 Mpa
bending strength		ISO 178	70.0 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	65.0 mg
Tensile modulus		ISO 527-2/1	2100 Mpa
Tensile strain	Break	ISO 527-2/50	30 %
Tensile strain		Yield	ISO 527-2/50	3.0 %
tensile strength	Yield	ISO 527-2/50	40.0 Mpa
tensile strength		Break	ISO 527-2/50	40.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Dissipation factor	50 Hz	IEC 60250	4.0E-4
		60 Hz	IEC 60250	4.0E-4
		1 MHz	IEC 60250	1.0E-3
Relative permittivity	50 Hz	IEC 60250	2.70
		1 MHz	IEC 60250	2.60
		60 Hz	IEC 60250	2.70
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.060 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
Charpy Notched Impact Strength	23°C	ISO 179/1eA	17 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	10 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	17 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
UL flame retardant rating	1.6 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE US/PX1112-701
drying temperature			100 to 120 °C
drying time			2.0 to 3.0 hr
Hopper temperature			60 to 80 °C
Mold temperature			80 to 120 °C
Processing (melt) temperature			280 to 300 °C
Spray nozzle temperature			260 to 280 °C
Temperature at the front of the material cylinder			280 to 300 °C
Temperature at the rear of the barrel			240 to 260 °C
Temperature in the middle of the barrel			260 to 280 °C