PA66 TS150G6F5A 浙江新力
--
高流动性,高模量,耐热好,尺寸稳定
塑壳断路器外壳,机构手柄,防护罩
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS150G6F5A |
|---|---|---|---|
| Tensile strength at break | IS0527 | 130 Mpa | |
| Yield bending strength | IS0178 | 210 Mpa | |
| Flexural modulus | IS0178 | 8500 Mpa | |
| elongation at break | IS0527 | 2 % | |
| Impact strength of simply supported beam without notch | IS0179 | 60 kJ/m² | |
| Charpy Notched Impact Strength | IS0179 | 9.0 kJ/m² |
| other | Test Condition | Test Method | 浙江新力/TS150G6F5A |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.00E+13 Ω | |
| proof tracking index | 3mm | IEC 60112 | 250 V |
| Linear forming shrinkage rate | IS02577 | 0.6 % |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS150G6F5A |
|---|---|---|---|
| GWIT | 厚度0.8mm | IEC 60695-2-13 | ℃ |
| Flame retardant performance | 厚度1.5mm | UL 94 | V-0 ℃ |
| 厚度0.8mm | UL 94 | ℃ | |
| GWFI | 厚度2.0mm | IEC 60695-2-12 | ℃ |
| Flame retardant performance | 厚度3.0mm | UL 94 | ℃ |
| 厚度2.0mm | UL 94 | ℃ | |
| GWFI | 厚度1.5mm | IEC 60695-2-12 | 960 ℃ |
| 厚度3.0mm | IEC 60695-2-11 | ℃ | |
| 厚度0.8mm | IEC 60695-2-12 | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS150G6F5A |
|---|---|---|---|
| density | IS01183 | 1.58 g/cm³ | |
| Water absorption rate | IS062 | 1.0 % |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS150G6F5A |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa | IS076 | 210 ℃ |
| 0.45MPa | IS076 | ℃ |