Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC B-7110R TEIJIN JAPAN
PANLITE®
Electronic field,Electrical field
Carbon fiber reinforced,High rigidity, Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| Water absorption rate | 水中24hr,23℃ | ASTM D-570 | 0.16 % |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| Tensile modulus | ASTM D-638 | 6860(70000) MPa(Kgf/cm | |
| Rockwell hardness | ASTM D-785 | 78 M标度 | |
| Impact strength of cantilever beam gap | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 70(7) J/m(kgf·cm/cm) |
| elongation | 断裂 | ASTM D-638 | 3 |
| tensile strength | 断裂点 | ASTM D-638 | 113(1150) MPa(Kgf/cm |
| Impact strength of cantilever beam gap | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 70(7) J/m(kgf·cm/cm) |
| Flexural modulus | ASTM D-790 | 6860(70000) MPa(Kgf/cm | |
| bending strength | ASTM D-570 | 157(1600) MPa(Kgf/cm |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 10 |
| processability | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| Shrinkage rate | 垂直方向 | ASTM D-955 | 0.3-0.5 % |
| 流动方向 | ASTM D-955 | 0.05-0.15 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| transmittance | 厚度3mm | ASTM D-1003 | 黑色 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/B-7110R |
|---|---|---|---|
| Linear coefficient of thermal expansion | 垂直方向 | ASTM D-696 | 7.1 |
| TEMPERATURE | 电学式，厚度1.47mm | UL 746B | 75 °C |
| Linear coefficient of thermal expansion | 流动方向 | ASTM D-696 | 3.3 |
| TEMPERATURE | 非冲击式，厚度1.47mm | UL 746B | 75 °C |
| 冲击式，厚度1.47mm | UL 746B | 75 °C | |
| Heat distortion temperature | 负荷1.813MPa(18.6kgf/cm)，HDT | ASTM D-648 | 147 °C |