GPPS MW-1-301 DENKA JAPAN
STYROL
Food service sector
high strength、transparent、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/MW-1-301 |
|---|---|---|---|
| melt mass-flow rate | 200℃,49N | ISO 1133 | 1.9 g/10min |
| density | 23℃ | ISO 1183 | 1050 kg/m |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/MW-1-301 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 100 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 75 kg·cm/cm(J/M)ft·lb/in | |
| Tensile stress | 5mm/min，断裂 | ISO 527-1 | 47 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2 | 75 M |
| Charpy Notched Impact Strength | 缺口,23℃ | ISO 179 | 2.8 KJ/m |
| elongation at break | ASTM D638/ISO 527 | 3300 % | |
| tensile strength | ASTM D638/ISO 527 | 47 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 2mm/min | ISO 178 | 100 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 3300 Mpa |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/MW-1-301 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1050 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 1.9 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/MW-1-301 |
|---|---|---|---|
| vicat | ASTM D1525/ISO R306 | 93 ℃（℉） | |
| 50N | ISO 306 | 93 °C | |
| Heat distortion temperature | 1.80MPa Flatwise method | ISO 75-1 | 74 °C |