Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM HC750 ASAHI JAPAN
TENAC™-C
Automotive sector、Electrical field、Electronic field、Household goods、Industrial applications
copolymer、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/HC750
Melt mass flow rate
ASTM D1238
g/10min
Melt mass flow rate
190℃/2.16kg
ISO 1133
g/10min
Shrinkage rate
Across Flow
ISO 294-4
%
Shrinkage rate
ASTM D955
%
1
Water absorption rate
24 hr
ASTM D570
%
Mechanical performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/HC750
Charpy notch impact strength
23℃
ISO 179/1eA
kJ/m²
Izod notch impact strength
ASTM D256
J/m
5
Tensile modulus
ISO 527-2
Mpa
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
3
tensile strength
ASTM D638
Mpa
Yield tensile stress
ISO 527-2
Mpa
elongation
断裂
ASTM D638
%
elongation
断裂
ISO 527-2
%
4
Bending modulus
ASTM D790
Mpa
bending strength
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/HC750
Hot deformation temperature
0.45MPa,unannealed
ASTM D648
℃
Hot deformation temperature
0.45MPa,unannealed
ISO 75-2/B
℃
Hot deformation temperature
1.8MPa,unannealed
ASTM D648
℃
Hot deformation temperature
1.8MPa,unannealed
ISO 75-2/A
℃
1