Electrical performance	Test Condition	BASF GERMANY/B3UM6 BK
dielectric constant	1MHz，干/湿	3.6/6
Compared to the Leakage Traceability Index (CTI)	干/湿	CTI 375
dielectric strength	K20/P50，干/湿	95/70 KV/mm
loss angle	1MHz，干/湿	0.02/0.3
Surface Resistivity	干/湿	10 Ω
Volume resistivity	干/湿	10 Ω.cm

Mechanical properties	Test Condition	BASF GERMANY/B3UM6 BK
Tensile creep modulus	1000h，湿	980 Mpa
Charpy Notched Impact Strength	+23℃，干/湿	20/30 KJ/m
Fracture stress (V=50mm/min)	干/湿	50/30 Mpa
Charpy Notched Impact Strength	30℃，干	20 KJ/m
ball-indentation hardness	干/湿	180/80 Mpa
elongation	≤0.5%, +23℃，湿	980 Mpa
Flexural modulus	干/湿	5200 Mpa
Charpy Notched Impact Strength	30℃，干/湿	3.5 KJ/m
Tensile yield stress (V=50mm/min)	干/湿	50/30 Mpa
Impact strength of cantilever beam gap	30℃，干	2 KJ/m
Impact Strength	+23℃，干/湿	30/55 J
Tensile modulus	干/湿	6000/3000 Mpa
Impact strength of cantilever beam gap	+23℃，干/湿	2/2.5 KJ/m
bending strength	干/湿	130/50 Mpa
elongation at break	干/湿，V=50mm/min	3/8 %

Thermal performance	Test Condition	BASF GERMANY/B3UM6 BK
TEMPERATURE	在20000h/5000h，后拉伸强度下降50%时	115/150 °C
Heat distortion temperature	1.8MPa负荷，干态，HDT	100 °C
thermal conductivity	干态	0.47 W/(m.K)
Linear coefficient of thermal expansion	（23-80）℃，干态	4-8/4-8
maximum service temperature		>200 °C
specific heat	干态	1.7 J/(g.K)
Heat distortion temperature	0.45MPa负荷,干态，HDT	200 °C