Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE 3220 FPC TAIWAN
TAISOX®
Stretch winding、film
antioxidant、Heat sealing performance、low density
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | FPC TAIWAN/3220 |
|---|---|---|---|
| tensile strength | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 35.3 Mpa |
| elongation | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 600 % |
| Secant modulus | 1%正割,MD:38µm,吹塑薄膜 | ASTMD882 | 147 Mpa |
| 1%正割,TD:38µm,吹塑薄膜 | ASTMD882 | 206 Mpa | |
| tensile strength | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 9.81 Mpa |
| Falling hammer impact | 38µm,吹塑薄膜 | ASTMD1709 | 120 g |
| elongation | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 800 % |
| Elmondov tear strength | MD:38µm,吹塑薄膜 | ASTMD1922 | 61 g |
| tensile strength | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 27.5 Mpa |
| Film thickness - tested | 38 µm | ||
| Elmondov tear strength | TD:38µm,吹塑薄膜 | ASTMD1922 | 650 g |
| tensile strength | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 10.8 Mpa |
| optical performance | Test Condition | Test Method | FPC TAIWAN/3220 |
|---|---|---|---|
| Haze ratio | 38.0µm,吹塑薄膜 | ASTMD1003 | 22 % |
| transparency | ASTMD1746 | 67.0 | |
| gloss | 45°,38.0µm,吹塑薄膜 | ASTMD2457 | 43 |
| physical property | Test Condition | Test Method | FPC TAIWAN/3220 |
|---|---|---|---|
| density | ASTMD1505 | 0.920 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | FPC TAIWAN/3220 |
|---|---|---|---|
| brittle temperature | ASTMD746 | -70.0 °C | |
| melting temperature | 122 °C | ||
| vicat | ASTMD1525 | 93.0 °C |