Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NH-1015 LOTTE KOREA
INFINO®
Engineering accessories,Automotive Applications
Chemical resistance,High rigidity,Thermal stability,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 44 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 40 kJ/m² |
| hardness | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| Tensile modulus | ISO 527-2/50 | 2500 Mpa | |
| bending strength | ISO 178 | 88.0 Mpa | |
| Flexural modulus | ISO 178 | 2450 Mpa | |
| bending strength | ASTM D790 | 86.0 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| Flexural modulus | ASTM D790 | 2400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 48.0 Mpa |
| Electrical performance | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| 2.0mm | UL 94 | 5VB | |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 775 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 23 g/10min |
| 220°C/10.0kg | ISO 1133 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/NH-1015 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 81.0 °C |
| vicat | -- | ISO 306/B120 | 100 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 93.0 °C |
| RTI Imp | 1.5mm | UL 746 | 85.0 °C |
| Heat distortion temperature | 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 93.0 °C |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| RTI Str | 1.5mm | UL 746 | 90.0 °C |
| RTI Elec | 1.5mm | UL 746 | 90.0 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 98.0 °C |