POM KD000 BKANT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 37 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.50 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 5.00 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 105 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 108 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3500 Mpa | |
| elongation | 断裂 | ASTM D638 | 7.2 % |
| tensile strength | 屈服 | ASTM D638 | 58.0 Mpa |
| 屈服 | ISO 527-2 | 53.0 Mpa | |
| bending strength | ISO 178 | 82.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| flexural modulus | ASTM D790 | 3250 Mpa | |
| Tensile modulus | ISO 527-2/1 | 3000 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.6 % |
| Tensile strain | 断裂 | ISO 527-2 | 20 % |
| bending strength | ASTM D790 | 95.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 54.0 Mpa |
| 断裂 | ISO 527-2 | 47.0 Mpa | |
| flexural modulus | ISO 178 | 3200 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+2to1.0E+4 ohms |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| shrinkage rate | MD：100°C | 内部方法 | 1.5-1.6 % |
| TD：100°C | 内部方法 | 1.1-1.2 % | |
| MD:24小时 | ISO 294-4 | 1.5-3.5 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.28 % |
| shrinkage rate | TD：24hr | ASTM D955 | 1.5-3.5 % |
| TD:24小时 | ISO 294-4 | 1.5-3.5 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.33 % |
| shrinkage rate | MD：60°C | 内部方法 | 1.2-1.3 % |
| MD：24hr | ASTM D955 | 1.5-3.5 % | |
| TD：60°C | 内部方法 | 0.90-1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/KD000 BKANT |
|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL 94 | HB |