PEI 1000F SABIC INNOVATIVE US
ULTEM™
Food service sector
Toughening、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD15255 | 219 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 201 °C |
| Linear thermal expansion coefficient | TD：-20to150°C | ASTME831 | 5.4E-05 cm/cm/°C |
| RTIElec | UL746 | 170 °C | |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 5.6E-05 cm/cm/°C |
| Thermal Conductivity | ASTMC177 | 0.22 W/m/K | |
| RTIStr | UL746 | 170 °C | |
| Evolution Calendar intelligent importer | UL746 | 170 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 210 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Rockwell Hardness | M级 | ASTMD785 | 109 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.25 % |
| Density / Specific Gravity | ASTMD792 | 1.27 g/cm³ | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 1.3 % |
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 9.0 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Poisson Ratio | ASTMD638 | 0.36 | |
| Tensile Elongation | 屈服 | ASTMD638 | 7.0 % |
| Flexural Strength | Yield,100mmSpan | ASTMD790 | 165 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 60 % |
| Flexural Modulus | 100mmSpan | ASTMD790 | 3520 Mpa |
| Tensile Modulus | ASTMD638 | 3590 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 110 Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Reverse Notch Izod Impact | 3.20mm | ASTMD256 | 1300 J/m |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 53 J/m |
| 23°C | ASTMD4812 | 1300 J/m | |
| Gardner Impact | 23°C | ASTMD3029 | 36.6 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | V-0 |
| 0.40mm | UL94 | V-2 | |
| Oxygen Index | ASTMD2863 | 47 % | |
| Flame Rating | 3.0mm | UL94 | 5VA |
| ASTME662 | 0.700 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000F |
|---|---|---|---|
| Dielectric Constant | 1kHz | ASTMD150 | 3.15 |
| Dissipation Factor? | 1kHz | ASTMD150 | 1.3E-03 |
| Volume Resistivity | ASTMD257 | 1E+17 ohms·cm | |
| Arc Resistance | ASTMD495 | PLC 5 | |
| Hot-wire Ignition | HWI | UL746 | PLC 1 |
| Dielectric Strength | 1.60mm,在油中 | ASTMD149 | 28 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 4 |
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| Dielectric Strength | 1.60mm,inAir | ASTMD149 | 33 KV/mm |
| Dissipation Factor? | 2.45GHz | ASTMD150 | 2.5E-03 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 2 |