PLA Kareline® PLMS6040 Plasthill Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 11 kJ/m² |
hardness | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
Rockwell hardness | R计秤,23°C | ISO 2039-2 | 122 |
Mechanical properties | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
tensile strength | ISO 527-2 | 75.0 MPa | |
Tensile strain | 断裂 | ISO 527-2 | 1.3 % |
Bending Strain | ISO 178 | 1.3 % | |
Flexural modulus | ISO 178 | 7400 MPa | |
bending strength | ISO 178 | 98.6 MPa |
flammability | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
Shrinkage rate | 0.20 % | ||
melt mass-flow rate | 200°C/10.0kg | ISO 1133 | 90 g/10min |
Water absorption rate | 平衡,23°C,50%RH | 1.1 % | |
Melt volume flow rate | 200°C/10.0kg | ISO 1133 | 76.8 cm³/10min |
density | ISO 1183 | 1.36 g/cm³ |
Thermal performance | Test Condition | Test Method | Plasthill Oy/Kareline® PLMS6040 |
---|---|---|---|
Continuous use temperature | -25.0-90.0 °C |