Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LC1402 IDEMITSU JAPAN
TARFLON™
Optical applications
High mobility、transparent、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 120 |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| ISO Shortcut | >PC< |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 15 % | |
| bending strength | ISO 178 | 100 Mpa | |
| Flexural modulus | ISO 178 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 65.0 Mpa |
| optical performance | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| transmissivity | ISO 13468-1 | 90.0 % | |
| refractive index | ASTM D542 | 1.585 | |
| Haze ratio | 3000µm | ASTM D1003 | 0.50 % |
| Yellowness Index | 0.95 YI |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 125 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.23 % |
| Shrinkage rate | MD:2.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/LC1402 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 130 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 120 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |