Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA A-6135 HN BK324 SOLVAY USA
AMODEL®
Shell、Vehicle electronics
Chemical resistance、Low moisture absorption
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/A-6135 HN BK324 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 62 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| hardness | Test Condition | Test Method | SOLVAY USA/A-6135 HN BK324 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 125 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/A-6135 HN BK324 |
|---|---|---|---|
| Tensile modulus | 175°C | ISO 527-2 | 5310 Mpa |
| 23°C | ISO 527-2 | 11500 Mpa | |
| tensile strength | 断裂,23°C | ISO 527-2 | 211 Mpa |
| 断裂,24°C | ISO 527-2 | 121 Mpa | |
| Flexural modulus | ASTM D790 | 11400 Mpa | |
| Tensile modulus | 150°C | ISO 527-2 | 6270 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 300 Mpa |
| elongation | 断裂 | ASTM D638 | 1.9 % |
| tensile strength | 断裂,150°C | ISO 527-2 | 92.4 Mpa |
| bending strength | 3.5%Strain,175°C | ISO 178 | 112 Mpa |
| Flexural modulus | 23°C | ISO 178 | 11400 Mpa |
| Poisson's ratio | 7.58 0.39 | ||
| bending strength | 3.5%Strain,150°C | ISO 178 | 123 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 4.9 % |
| bending strength | ASTM D790 | 310 Mpa | |
| Flexural modulus | 100°C | ISO 178 | 6600 Mpa |
| Tensile strain | 断裂,175°C | ISO 527-2 | 4.7 % |
| tensile strength | 断裂,175°C | ISO 527-2 | 82.0 Mpa |
| Tensile modulus | 100°C | ISO 527-2 | 7310 Mpa |
| tensile strength | ASTM D638 | 203 Mpa | |
| bending strength | 3.5%Strain,100°C | ISO 178 | 170 Mpa |
| Tensile strain | 断裂,24°C | ISO 527-2 | 4.3 % |
| Tensile modulus | ASTM D638 | 13800 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| Flexural modulus | 150°C | ISO 178 | 4900 Mpa |
| 175°C | ISO 178 | 4600 Mpa | |
| shear strength | ASTM D732 | 87.6 Mpa | |
| compressive strength | ASTM D695 | 148 Mpa |
| physical property | Test Condition | Test Method | SOLVAY USA/A-6135 HN BK324 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.60 % |
| TD | ISO 294-4 | 1.0 % | |
| MD | ISO 294-4 | 0.50 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.30 % |
| 23°C,24hr | ISO 62 | 0.29 % | |
| Shrinkage rate | TD | ASTM D955 | 0.90 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/A-6135 HN BK324 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1E-04 cm/cm/°C |
| melting temperature | ISO 11357-3 | 310 °C | |
| Heat distortion temperature | 1.8MPa,退火,3.20mm，HDT | ASTM D648 | 291 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 303 °C | |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.6E-05 cm/cm/°C |
| TD：0to100°C | ASTME831 | 6.1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 288 °C |
| melting temperature | ASTM D570 | 310 °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2.2E-05 cm/cm/°C |