PA66 A3X2G5 BK BASF SHANGHAI
Ultramid®
Bottle cap、Plastic cover、Home appliance components、Automotive Applications、Fitness equipment、Electronic and electrical
Electrical performance、Flame retardant、Oil resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/A3X2G5 BK |
|---|---|---|---|
| Kabi impact strength | 30℃，干 | 65 KJ/m | |
| Elongation at break (V=50mm/min) | 干/湿 | 3/4.5 % | |
| Tensile creep modulus | 1000h,湿 | 3500 Mpa | |
| Impact and destructive energy | 干/湿 | 4/10 J | |
| Tensile modulus of elasticity | 干/湿 | 8500/6000 Mpa | |
| Fracture stress (V=50mm/min) | 干/湿 | 140/100 Mpa | |
| elongation | ≤0.5%, +23℃，湿 | 3500 Mpa | |
| Flexural modulus | 干/湿 | 7100 Mpa | |
| Kapi notch impact strength | +23℃，干/湿 | 13/18 KJ/m | |
| Izo notch impact strength | +23℃，干/湿 | 11/17 KJ/m | |
| Kabi impact strength | +23℃，干/湿 | 70/75 KJ/m | |
| Yield elongation (V=50mm/min) | 干/湿 | 3/4.5 % | |
| 干/湿 | 190 Mpa |
| Electrical performance | Test Condition | Test Method | BASF SHANGHAI/A3X2G5 BK |
|---|---|---|---|
| 干/湿 | 10 Ω.cm | ||
| dielectric constant | 1MHz，干/湿 | 3.7/5 | |
| 干/湿 | CTI 600 M | ||
| loss angle | 1MHz，干/湿 | 0.02/0.1 | |
| dielectric strength | K20/P50，干/湿 | 80/65 KV/mm | |
| Surface Resistivity | 干/湿 | >10 Ω | |
| Relative arc track index CT1 | 干/湿 | CTI 500 |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/A3X2G5 BK |
|---|---|---|---|
| Specific heat capacity | 干态 | 1.5 J/(g.K) | |
| （23-80）℃，干态 | 2.5-3.5/6-8 10 | ||
| 1.8MPa负荷，干态 | 250 °C | ||
| 0.45MPa负荷，干态 | 250 °C | ||
| 在20000h/5000h，后拉伸强度下降50%时 | 135/153 °C | ||
| thermal conductivity | 干态 | 0.27 W/(m.K) | |
| Maximum operating temperature | 220 °C |