Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500P BK602 DUPONT USA
Delrin®
Automotive sector、Fitness equipment
High rigidity、Aging resistance、currency、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| -30°C | ISO 179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 180 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| -40°C | ISO 180/1A | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 160 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 3.10 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3100 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| Flexural modulus | ISO 178 | 3000 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 14 % |
| tensile strength | 屈服 | ISO 527-2 | 71.0 Mpa |
| Poisson's ratio | ISO 527 | 0.35 |
| flammability | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 90 % |
| G-value(condensate) | ISO 6452 | 3.5E-04 g | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | 24 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 2.0 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.3 % |
| density | ISO 1183 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 15 g/10min |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.40 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/500P BK602 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 162 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO 11359-2 | 160 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 96.0 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |