PPS A504X95 TORAY JAPAN

Torelina®

Automotive Applications,sporting goods

enhance,environment?protection

ULMSDS

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

Supplementary Information	Test Condition	Test Method	TORAY JAPAN/A504X95
BarFlowLength	320°C,1.00mm	Internal Method	150 mm

hardness	Test Condition	Test Method	TORAY JAPAN/A504X95
Rockwell hardness	R-Sale	ISO 2039-2	122

thermal performance	Test Condition	Test Method	TORAY JAPAN/A504X95
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	>260 ℃（℉）
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	260 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	3.1E-05 cm/cm/°C
			ASTM D696/ISO 11359	2.3 mm/mm.℃
		MD	ISO 11359-2	2.3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	278 °C
Melting temperature				278 ℃（℉）

mechanical properties	Test Condition	Test Method	TORAY JAPAN/A504X95
Bending modulus	23°C	ISO 178	15500 Mpa
Bending modulus			ASTM D790/ISO 178	15.5 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	290 kg/cm²(MPa)[Lb/in²]
bending strength		23°C	ISO 178	290 Mpa
Elongation at Break		ASTM D638/ISO 527	1.6 %
Friction coefficient			0.25
Impact strength of cantilever beam gap		ASTM D256/ISO 179	45 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	122
shear strength	23°C	JISK7214	75.0 Mpa
Taber abraser	1000Cycles	ISO 9352	50.0 mg
Tensile strain	Break,23°C	ISO 527-2	1.6 %
tensile strength		ASTM D638/ISO 527	200 kg/cm²(MPa)[Lb/in²]
tensile strength		23°C	ISO 527-2	200 Mpa

Electrical performance	Test Condition	Test Method	TORAY JAPAN/A504X95
Dielectric constant		ASTM D150/IEC 60250	3.6
Dielectric constant		23°C,1MHz	IEC 60250	3.60
Dielectric strength		IEC 60243-1	25 KV/mm
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Volume resistivity		IEC 60093	1E+16 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	1014 Ω.cm

other	Test Condition	Test Method	TORAY JAPAN/A504X95
characteristic			40%加纤.增强.低光泽

Physical properties	Test Condition	Test Method	TORAY JAPAN/A504X95
density		ASTM D792/ISO 1183	1.66
Shrinkage rate	TD:3.00mm3	Internal Method	0.80 %
			ASTM D955	0.2 %
		MD:3.00mm4	Internal Method	0.20 %
Water absorption rate	23°C,24hr	ISO 62	0.020 %
Water absorption rate			ASTM D570/ISO 62	0.02 %

impact performance	Test Condition	Test Method	TORAY JAPAN/A504X95
Impact strength of simply supported beam without notch	23°C	ISO 179	45 kJ/m²

flammability	Test Condition	Test Method	TORAY JAPAN/A504X95
UL flame retardant rating	0.28mm	UL 94	V-0