PPX 7110-BL4A061 BK SABIC INNOVATIVE US
NORYL PPX™
electromagnetic shielding
Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/7110-BL4A061 BK |
|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 27.8 J |
| 23°C,TotalEnergy | ASTMD3763 | 38.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/7110-BL4A061 BK |
|---|---|---|---|
| elongation | 屈服 | ASTMD638 | 6.5 % |
| 断裂 | ASTMD638 | 200 % | |
| Bending strength 5 | 屈服,50.0mm跨距 | ASTMD790 | 51.7 Mpa |
| tensile strength | 屈服 | ASTMD638 | 35.9 Mpa |
| 断裂 | ASTMD638 | 32.4 Mpa | |
| Tensile modulus 1 | ASTMD638 | 1340 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 1550 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/7110-BL4A061 BK |
|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/7110-BL4A061 BK |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80到1.2 % |
| melt mass-flow rate | 260°C/5.0kg | ASTMD1238 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/7110-BL4A061 BK |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 77.2 °C | |
| MD:-40到40°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| RTI Elec | UL746 | 50.0 °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 113 °C | |
| TD:-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| RTI | UL746 | 50.0 °C | |
| vicat | ASTMD15256 | 139 °C | |
| RTI Imp | UL746 | 50.0 °C |