Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA/PC XTPMFR10-WH5F007 SABIC INNOVATIVE SAUDI
GELOY™
Automotive Applications,Electrical applications
Thermal stability,Antistatic,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 | ISO 75-2/Af | 81.0 °C |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 | ISO 75-2/Bf | 90.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B120 | 98.0 °C |
| -- | ISO 306/B50 | 96.0 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| Bending modulus | ISO 178 | 2720 Mpa | |
| bending strength | ISO 178 | 97.0 Mpa | |
| elongation | 断裂 | ISO 527-2/5 | 50 % |
| 屈服3 | ASTM D638 | 4.0 % | |
| 屈服4 | ASTM D638 | 4.0 % | |
| 断裂3 | ASTM D638 | 31 % | |
| 断裂4 | ASTM D638 | 58 % | |
| 屈服 | ISO 527-2/5 | 4.0 % | |
| 断裂 | ISO 527-2/50 | 21 % | |
| Tensile modulus | --2 | ASTM D638 | 2680 Mpa |
| -- | ISO 527-2/1 | 2680 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 46.0 Mpa |
| 断裂 | ISO 527-2/50 | 47.0 Mpa | |
| 断裂4 | ASTM D638 | 49.0 Mpa | |
| 屈服 | ISO 527-2/5 | 61.0 Mpa | |
| 断裂3 | ASTM D638 | 47.0 Mpa | |
| 屈服4 | ASTM D638 | 60.0 Mpa | |
| 屈服 | ISO 527-2/50 | 66.0 Mpa | |
| 屈服3 | ASTM D638 | 65.0 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 30.0 cm3/10min |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 85.0 J |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| UL flame retardant rating | 1.0 mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| Melt viscosity | 260°C, 1500 sec^-1 | ISO 11443 | 105 Pa·s |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/XTPMFR10-WH5F007 |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Hopper temperature | 60 to 80 °C | ||
| Mold temperature | 50 to 70 °C | ||
| Processing (melt) temperature | 230 to 270 °C | ||
| Spray nozzle temperature | 220 to 260 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature at the front of the material cylinder | 230 to 270 °C | ||
| Temperature at the rear of the barrel | 200 to 230 °C | ||
| Temperature in the middle of the barrel | 220 to 260 °C |