Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 1100N OPP OMAN
--
Household goods
Homopolymer,High temperature resistan,high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | OPP OMAN/1100N |
|---|---|---|---|
| melt mass-flow rate | 230℃，2.16kg | ISO 1133 | 12 g/10min |
| Shrinkage rate | 1.4 % | ||
| density | ISO 1183 | 0.91 g/cm³ |
| Mechanical properties | Test Condition | Test Method | OPP OMAN/1100N |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 3.0 Kj/cm2 |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 110 Kj/cm2 |
| elongation at break | 50mm/min | ISO 527 | 9 % |
| Charpy Notched Impact Strength | -20℃ | ISO 179/1eU | 14 Kj/cm2 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 76 Mpa |
| tensile strength | 50mm/min | ISO 527 | 36 Mpa |
| Flexural modulus | 1mm/min | ISO 527 | 1550 Mpa |
| Charpy Notched Impact Strength | 0℃ | ISO 179/1eU | 25 Kj/cm2 |
| Thermal performance | Test Condition | Test Method | OPP OMAN/1100N |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa，HDT | ISO 75 | 54 °C |
| vicat | A/120 10N | ISO 306 | 155 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75 | 85 °C |