ASA HRA222 SABIC INNOVATIVE US

GELOY™

Electrical appliances,Electronic field,Electrical field

UV resistance,Flame retardant

UL

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/HRA222
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	99.0 °C
Hot deformation temperature		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	88.0 °C
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	6.9E-5 cm/cm/°C
		Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5 cm/cm/°C
		Across Flow : -30 to 80°C	ISO 11359-2	7.1E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	104 °C
		--	ISO 306/B50	102 °C
		--	ISO 306/A50	111 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/HRA222
Bending modulus		ISO 178	2510 Mpa
bending strength		ISO 178	93.0 Mpa
elongation	Yield	ISO 527-2/50	4.4 %
		Break	ISO 527-2/5	> 50 %
		Yield5	ASTM D638	4.2 %
		Yield4	ASTM D638	4.3 %
		Break4	ASTM D638	> 100 %
		Break5	ASTM D638	> 100 %
		Yield	ISO 527-2/5	4.3 %
Tensile modulus	--3	ASTM D638	2590 Mpa
Tensile modulus		--	ISO 527-2/1	2520 Mpa
tensile strength	Break	ISO 527-2/5	51.0 Mpa
		Yield	ISO 527-2/50	60.0 Mpa
		Break	ISO 527-2/50	45.0 Mpa
		Break4	ASTM D638	56.0 Mpa
		Break5	ASTM D638	66.0 Mpa
		Yield	ISO 527-2/5	62.0 Mpa
		Yield5	ASTM D638	59.0 Mpa
		Yield4	ASTM D638	63.0 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/HRA222
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.60 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.20 %

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/HRA222
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	29 %
UL flame retardant rating	2.3 mm	UL 94	5VB
		0.8 mm	UL 94	V-2
		2.0 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE US/HRA222
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Hopper temperature			60 to 80 °C
Mold temperature			50 to 70 °C
Processing (melt) temperature			230 to 270 °C
Spray nozzle temperature			220 to 260 °C
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			230 to 270 °C
Temperature at the rear of the barrel			200 to 230 °C
Temperature in the middle of the barrel			220 to 260 °C