PES JF1006 BK81565 SABIC INNOVATIVE US
LNP™ THERMOCOMP™ 
Electronic field、mechanical、Bearing retainer
High temperature creep re、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/JF1006 BK81565
Suspended wall beam without notch impact strength23°CISO 180/1U40 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-24.16 J
Impact strength of cantilever beam gap23°CISO 180/1A9.5 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376310.7 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/JF1006 BK81565
Tensile modulusISO 527-2/19450 Mpa
bending strengthASTM D790210 Mpa
Wear factorWasherASTM D3702Modified170 10^-10in^5-min/ft-lb-hr
tensile strength 断裂ASTM D638143 Mpa
断裂ISO 527-2136 Mpa
Flexural modulusASTM D7909720 Mpa
Tensile modulusASTM D63810800 Mpa
elongation断裂ASTM D6382.2 %
bending strengthISO 178208 Mpa
coefficient of frictionStaticASTM D3702Modified0.57
Tensile strain断裂ISO 527-22.1 %
Flexural modulusISO 17810000 Mpa
coefficient of frictionDynamicASTM D3702Modified0.52
physical property Test ConditionTest MethodSABIC INNOVATIVE US/JF1006 BK81565
Shrinkage rateMD:24小时ISO 294-40.27 %
MD：24小时ASTM D9550.30 %
Water absorption rate24hr,50%RHASTM D5700.34 %
平衡,23°C,50%RHISO 620.46 %
Shrinkage rateTD：24hrASTM D9550.50 %
TD:24小时ISO 294-40.48 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/JF1006 BK81565
Linear coefficient of thermal expansionTD：-40到40°CASTME8313.6E-05 cm/cm/°C
TD：-40到40°CISO 11359-23.7E-05 cm/cm/°C
MD：-40到40°CASTME8313.1E-05 cm/cm/°C
MD：-40到40°CISO 11359-23.1E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af210 °C
1.8MPa,未退火,3.20mm，HDTASTM D648210 °C