Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 3020U UBE JAPAN
UBESTA
Electric wire、Cable、Medical Supplies、disposable、Food service sector、Optical level
Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | UBE JAPAN/3020U |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 59 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D412/ISO 527 | 5 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D412/ISO 527 | ＞200 % | |
| tensile strength | ASTM D412/ISO 527 | 45 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | 屈服 | ISO 527-1/-2 | 5 % |
| Rockwell hardness | ASTM D785 | 105 | |
| tensile strength | 屈服 | ISO 527-1/-2 | 45 Mpa |
| elongation | 断裂 | ISO 527-1/-2 | ＞200 % |
| bending strength | ISO 178 | 59 Mpa | |
| Flexural modulus | ISO 178 | 1500 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 4C KJ/m |
| -40℃ | ISO 179/1eA | 4C KJ/m | |
| Flexural modulus | ASTM D412/ISO 527 | 1500 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ISO 2039-2 | 105 R | |
| Shore hardness | ISO 868 | 78 D |
| Electrical performance | Test Condition | Test Method | UBE JAPAN/3020U |
|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 1015 Ω.cm | |
| IEC 60093 | 10 Ω.cm |
| Physical properties | Test Condition | Test Method | UBE JAPAN/3020U |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.9/1.1 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 20 g/10min | |
| density | ASTM D792/ISO 1183 | 1.02 kg·cm/cm(J/M)ft·lb/in |
| physical property | Test Condition | Test Method | UBE JAPAN/3020U |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.7 % | |
| Shrinkage rate | ISO 294-4 | 0.9/1.1 % | |
| melt mass-flow rate | ISO 1133 | 20 g/10min | |
| melting temperature | ISO 11357-3 | 178 °C |
| Thermal performance | Test Condition | Test Method | UBE JAPAN/3020U |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.3 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 47 ℃（℉） |
| 1.8Mpa，HDT | ISO 75-2 | 47 °C | |
| 0.45Mpa，HDT | ISO 75-2 | 92 °C | |
| melting temperature | 178 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.3 mm/mm.℃ |