PPS TS201 TOYOBO JAPAN
--
--
dimensional stability 、High rigidity、Filler: Glass mineral
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 121 |
Electrical performance | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
Dissipation Factor | 1kHz | ASTM D150 | 0.055 |
Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
dielectric constant | 1kHz | ASTM D150 | 5.10 |
Dissipation Factor | 1MHz | ASTM D150 | 8.5E-03 |
arc resistance | ISO 14782 | 137 | |
dielectric strength | ASTM D149 | 11 KV/mm | |
dielectric constant | 1MHz | ASTM D150 | 4.50 |
arc resistance | ASTM D495 | 137 sec |
Mechanical properties | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 2390 kg/cm²(MPa)[Lb/in²] | |
Tensile modulus | ASTM D638 | 21600 Mpa | |
elongation | 断裂 | ASTM D638 | 1.4 % |
Flexural modulus | ASTM D790/ISO 178 | 19*10^4 kg/cm²(MPa)[Lb/in²] | |
bending strength | 屈服 | ASTM D790 | 234 Mpa |
Tensile modulus | ASTM D638/ISO 527 | 22*10^4 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 屈服 | ASTM D638 | 170 Mpa |
ASTM D638/ISO 527 | 1730 kg/cm²(MPa)[Lb/in²] | ||
Flexural modulus | ASTM D790 | 18600 Mpa |
other | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
characteristic | 玻璃纤维和无机物填充增强等级.高硬度.尺寸稳定性.可以代替金属材料 |
Physical properties | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.96 | |
Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
flammability | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
UL flame retardant rating | UL 94 | V-0 |
physical property | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 0.15 % |
Water absorption rate | 24hr | ASTM D570 | 0.020 % |
Shrinkage rate | TD | ASTM D955 | 0.45 % |
Thermal performance | Test Condition | Test Method | TOYOBO JAPAN/TS201 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 260 °C |
Linear coefficient of thermal expansion | TD | ASTM D696 | 4.8E-05 cm/cm/°C |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | >260 ℃(℉) |
Linear coefficient of thermal expansion | MD | ASTM D696 | 1.2E-05 cm/cm/°C |