PA66 A3 ICF 30 AKRO-PLASTIC GERMANY
AKROMID®
--
Filler: Carbon fiber rein、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 55 kJ/m² |
| -30°C | ISO179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| ReinforcementContent | ISO1172 | 30 % |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 220 Mpa |
| Tensile modulus | ISO527-2/1 | 23000 Mpa | |
| Tensile strain | 断裂 | ISO527-2/5 | 2.0 % |
| Bending modulus 2 | ISO178 | 22000 Mpa | |
| Bending stress 2 | ISO178 | 370 Mpa | |
| Fracture bending strain 3 | ISO178 | 2.5 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+04 ohms |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.70 % |
| HumidityAbsorption-62%RH | 70°C | ISO1110 | 1.9 % |
| Shrinkage rate | MD | ISO294-4 | 0.20 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3 ICF 30 |
|---|---|---|---|
| thermal conductivity | DIN52612 | 0.42 W/m/K | |
| 1.8MPa,未退火 | ISO75-2/A | 254 °C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 cm/cm/°C | |
| MD：23到80°C | ISO11359-2 | 6E-06 cm/cm/°C | |
| Melting temperature 5 | DINEN11357-1 | 262 °C |