PC/ABS NX11302 WH9E641 SABIC INNOVATIVE NANSHA
CYCOLOY™
Plastic bag,Gears,Casters
High mobility,High impact resistance,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX11302 WH9E641 |
|---|---|---|---|
| Dissipation Factor | 1.00GHz | IEC 60250 | 5.7E-03 |
| relative permittivity | 1.00GHz | IEC 60250 | 2.94 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX11302 WH9E641 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2350 Mpa | |
| elongation | 断裂 | ASTM D638 | 75 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 79.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.6 % |
| tensile strength | 断裂 | ASTM D638 | 46.0 Mpa |
| 屈服 | ASTM D638 | 47.0 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2230 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 78.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX11302 WH9E641 |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.010 % |
| 24hr | ASTM D570 | 0.010 % | |
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.60 % |
| MD:24小时 | ASTM D955 | 0.60 % | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/NX11302 WH9E641 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 106 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |