Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RAL23-YWLTNAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components、Electronic and electrical
High temperature resistan、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RAL23-YWLTNAT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 37 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RAL23-YWLTNAT |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3800 Mpa | |
| bending strength | ASTM D790 | 131 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 89.6 Mpa |
| 断裂 | ISO 527-2 | 85.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 23.0 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 3940 Mpa | |
| Tensile modulus | ASTM D638 | 3680 Mpa | |
| elongation | 断裂 | ASTM D638 | 5.9 % |
| bending strength | ISO 178 | 107 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.32 |
| Tensile strain | 断裂 | ISO 527-2 | 6.3 % |
| Flexural modulus | ISO 178 | 3500 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.38 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RAL23-YWLTNAT |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 1.7-1.8 % |
| density | ASTM D792 | 1.24 g/cm³ | |
| ISO 1183 | 1.23 g/cm³ | ||
| Shrinkage rate | TD：24hr | ASTM D955 | 2.0-2.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RAL23-YWLTNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 9.7E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 9.8E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |