LLDPE SP0540 MITSUI CHEM JAPAN
EVOLUE™
Stretch winding、film、Laminate
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 无断裂 |
| hardness | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 49 |
| Basic performance | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 3.8 g/10min |
| density | ISO 1183 | 0.903 g/cm³ |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | No Break | |
| Tensile stress | Injection Molded，断裂 | ISO 527-2 | >16 MPa |
| Tensile strain | 断裂 | ISO 527-2 | >500 % |
| Flexural modulus | ISO 178 | 120 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | >16.0 Mpa |
| Tensile strain | Injection Molded，断裂 | ISO 527-2 | >500 % |
| Shore hardness | Shore D，Injection Molded | ISO 868 | 49 |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| Environmental stress cracking resistance | ASTM D1693 | >1000 hr | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.8 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/SP0540 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 98 ℃ | |
| ISO 11357-3 | 98.0 °C | ||
| vicat | ISO 306 | 83.0 °C | |
| ISO 306 | 83 ℃ |