POM 2013A ASAHI JAPAN
TENAC™
Automotive external components,roller,Pipeline accessories
Ultra high viscosity,Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/2013A
bending strengthASTM D790/ISO 17893 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gapASTM D256/ISO 179127 kg·cm/cm(J/M)ft·lb/in
Flexural modulusASTM D790/ISO 1782740 kg/cm²(MPa)[Lb/in²]
Rockwell hardnessASTM D78594 M
bending strengthASTM D79093 Mpa
wear resistanceASTM D104413
elongationASTM D638/ISO 52770 %
elongation at breakASTM D638/ISO 52770 %
Impact strength of cantilever beam gapASTM D256127 J/m
Rockwell hardnessASTM D78594
Flexural modulusASTM D7902740 Mpa
elongation at breakASTM D63870 %
tensile strength ASTM D638/ISO 52767 kg/cm²(MPa)[Lb/in²]
ASTM D63867 Mpa
Rockwell hardnessASTM D785120 R
otherTest ConditionTest MethodASAHI JAPAN/2013A
characteristic汽车部件
Physical propertiesTest ConditionTest MethodASAHI JAPAN/2013A
Shrinkage rateASTM D9551.8-2.2 %
densityASTM D792/ISO 11831.42
melt mass-flow rateASTM D1238/ISO 11331.7 g/10min
Water absorption rateASTM D570/ISO 620.2 %
physical property Test ConditionTest MethodASAHI JAPAN/2013A
Shrinkage rate垂直方向旭化成法1.8-2.2 %
平行方向旭化成法1.8-2.2 %
Water absorption rateASTM D5700.2 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/2013A
melt mass-flow rateASTM D12381.7 g/10min
Heat distortion temperature0.45MPa，HDTASTM D648172 °C
HDTASTM D648/ISO 75172 ℃（℉）
1.82MPa，HDTASTM D648136 °C
Linear coefficient of thermal expansionTMA法10