EVOH EVAL™ M100B EVAL Europe nv
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -- | ISO 179 | 2.0 kJ/m² |
| -40°C | ISO 179 | 3.0 kJ/m² |
| hardness | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 97 |
| film | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| OTr | 20°C,85%RH | ISO 14663-2 | 0.016 cm³·mm/m²/atm/24hr |
| 20°C,35%RH | ISO 14663-2 | 1E-03 cm³·mm/m²/atm/24hr | |
| 20°C,100%RH | ISO 14663-2 | 0.042 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ASTME96 | 3.4 g·mm/m²/atm/24hr | |
| OTr | 20°C,0%RH | ISO 14663-2 | 1E-03 cm³·mm/m²/atm/24hr |
| 20°C,65%RH | ISO 14663-2 | 2E-03 cm³·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 14 % |
| Tensile modulus | ISO 527-2 | 3200 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 45.0 MPa |
| Flexural modulus | ISO 178 | 4800 MPa |
| physical property | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 4.9 g/10min |
| 210°C/2.16kg | ISO 1133 | 2.2 g/10min | |
| Ethylene content | 内部方法 | 24.0 mol% | |
| density | ISO 1183 | 1.22 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 3.8 g/10min |
| Thermal performance | Test Condition | Test Method | EVAL Europe nv/EVAL™ M100B |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 195 °C | |
| Crystallization peak temperature | ISO 11357-3 | 168 °C | |
| vicat | ISO 306 | 186 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |