PC/ABS TMB1412 MITSUBISHI ENGINEERING JAPAN
IUPILON™
--
--
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 150 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 4100 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 10 % | |
| bending strength | ISO 178 | 100 Mpa | |
| Flexural modulus | ISO 178 | 4200 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 2.6 % |
| tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.15-0.35 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 20.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.15-0.35 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.20 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/TMB1412 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 89.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 79.0 °C |