ABS PA-765B TAIWAN CHIMEI
POLYLAC® 
Home appliance components,Fitness equipment,Electronic field,Electrical field
Flame retardant,Medium impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
Rockwell hardnessR-ScaleASTM D785102
thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
Hot deformation temperature1.8MPa,UnannealedASTM D64876.0 °C
1.8MPa,UnannealedISO 75-2/A77.0 °C
1.8MPa,AnnealedASTMD64885.0 °C
Linear coefficient of thermal expansionMDISO 11359-28.6E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B5080.0 °C
--ASTM D1525792.0 °C
--ISO 306/A5094.0 °C
mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
Bending modulus--5ASTM D7902340 Mpa
--6ISO 1781800 Mpa
bending strength--5ASTM D79063.4 Mpa
--6ISO 17857.0 Mpa
elongationBreak4ASTM D63825 %
BreakISO 527-2/5010 %
tensile strengthYieldISO 527-2/5038.0 Mpa
BreakISO 527-2/5029.0 Mpa
Yield4ASTM D63839.1 Mpa
Physical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
density23°CISO 11831.16 g/cm³
--3ASTM D7921.16 g/cm³
melt mass-flow rate200°C/5.0kgASTM D12384.2 g/10min
Melt Volume Flow Rate (MVR)220°C/10.0kgISO 113338.0 cm3/10min
Shrinkage rateISO 294-40.30-0.60 %
impact performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
Charpy Notched Impact Strength-30°CISO 17911 kJ/m²
23°CISO 17926 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A11 kJ/m²
23°CISO 180/1A24 kJ/m²
23°C,3.20mmASTM D256250 J/m
23°C,6.40mmASTM D256210 J/m
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-765B
UL flame retardant rating2.5mmUL 94V-0
3.0mmUL 945VA
1.5mmUL 94V-2