Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM GF705 KOLON KOREA
KOCETAL®
--
high strength、High rigidity、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 70 J/m |
| hardness | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 90 |
| M级 | ISO 2039-2 | 96 |
| Electrical performance | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 6E-03 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| dielectric constant | ASTM D150 | 3.70 |
| Mechanical properties | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 200 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 140 Mpa |
| Flexural modulus | 23°C | ISO 178 | 8700 Mpa |
| bending strength | 23°C | ASTM D790 | 220 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 147 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 7.0 % |
| Flexural modulus | 23°C | ASTM D790 | 7800 Mpa |
| flammability | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50 % |
| TD | ISO 294-4 | 1.2 % | |
| MD | ISO 294-4 | 0.64 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| 平衡,23°C,60%RH | ASTM D570 | 0.20 % | |
| density | ASTM D792 | 1.59 g/cm³ | |
| ISO 1183 | 1.59 g/cm³ | ||
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 10 g/10min |
| 190°C/2.16kg | ASTM D1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | KOLON KOREA/GF705 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 163 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 164 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 162 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2.5E-05 cm/cm/°C |
| melting temperature | 166 °C |