Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CX7240-701 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electrical field、Electronic field、Architectural application、Outdoor applications、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Aerospace Applications、Liquid handling
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C9 | ISO 180/1A | 10 kJ/m² |
| -30°C | ASTM D256 | 180 J/m | |
| 23°C | ASTM D256 | 700 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| Impact strength of cantilever beam gap | 23°C9 | ISO 180/1A | 25 kJ/m² |
| Charpy Notched Impact Strength | 23°C7 | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C10 | ISO 180/1A | 10 kJ/m² |
| Charpy Notched Impact Strength | 23°C8 | ISO 179/1eA | 22 kJ/m² |
| Impact strength of cantilever beam gap | 23°C10 | ISO 180/1A | 20 kJ/m² |
| Charpy Notched Impact Strength | -30°C7 | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.1 % |
| tensile strength | 断裂 | ASTM D638 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2500 Mpa |
| Tensile modulus | ASTM D638 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| elongation | 断裂 | ASTM D638 | 100 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 104 Mpa |
| ISO 178 | 96.0 Mpa | ||
| Flexural modulus | ISO 178 | 2500 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 65.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 90 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm13 | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 0.75mm13 | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Hot filament ignition temperature | 0.75mm13 | IEC 60695-2-13 | 775 °C |
| 3.0mm | IEC 60695-2-13 | 800 °C | |
| 1.0mm | IEC 60695-2-13 | 825 °C | |
| 1.5mm13 | IEC 60695-2-13 | 775 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 35 % | |
| UL flame retardant rating | 1.5mm | UL 94 | 5VB |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.60mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.20 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 15.0 cm3/10min |
| density | ASTM D792 | 1.19 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-701 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 99.0 °C |
| vicat | ASTM D152512 | 110 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 100 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| RTI Str | UL 746 | 90.0 °C | |
| vicat | -- | ISO 306/B120 | 113 °C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 110 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 93.0 °C |
| RTI Imp | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 89.0 °C |
| RTI Elec | UL 746 | 90.0 °C |