Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1300S ASAHI JAPAN
Leona™
Laptop case、Automotive sector、parts、Consumer goods sector
High mobility、High rigidity、Good flexibility
UL
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 26 % |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 80 M（Scale） | |
| ASTM D785 | 120 R |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 39(147) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 2.8(1.2) GPa |
| bending strength | 23°C | ASTM D790 | 118 Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 79(57) Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 2790 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 118 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] | |
| Wear factor | 湿 | ASTM D-1044 | 7 |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) R scale |
| 干(湿) | ASTM D-785 | 80(55) M Scale | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 39 J/m |
| bending strength | 干(湿) | ASTM D-790 | 118(54) Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 39 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | 23°C | ASTM D638 | 50 % |
| Flexural modulus | 23°C | ASTM D790 | 2800 Mpa |
| tensile strength | 23°C | ASTM D638 | 79 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 50(250) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| dielectric strength | ASTM D149 | 20 KV/mm | |
| Volume resistivity | ASTM D257/IEC 60093 | 10-10 Ω.cm | |
| Dissipation Factor | 相对漏电起痕指数 | ASTM D3638 | 600 V |
| other | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| characteristic | 标准.流动 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.14 | |
| Water absorption rate | ASTM D570/ISO 62 | 2.5 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-2 0.40mm | |
| Limiting Oxygen Index | ASTM2863 | 26 % | |
| UL flame retardant rating | UL -94 | V-2 0.71mm | |
| UL -94 | V-2 1.50mm | ||
| UL -94 | V-2 3.00mm |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Shrinkage rate | MD2.0mm | ASTM D995 | 1.3 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 2.5 % |
| Shrinkage rate | TD2.0mm | ASTM D995 | 2.0 % |
| 干 | 旭化成方法 | 1.3-2.0 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1300S |
|---|---|---|---|
| Combustibility (rate) | UL 94 | v-2 | |
| specific heat | 干 | 1670 J/(kg.k) | |
| Linear coefficient of thermal expansion | 比热 | 1670 J/kg/°C | |
| 干 | ASTM D-696 | 8 | |
| ASTM D696/ISO 11359 | 8 mm/mm.℃ | ||
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D-648 | 70 °C |
| HDT | ASTM D648/ISO 75 | 230 ℃（℉） | |
| 0.46MPa,干，HDT | ASTM D-648 | 230 °C | |
| thermal conductivity | 干 | 0.2 W/(m.K) | |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 70 °C |
| UL flame retardant rating | 干 | UL 94 | V-2 |
| Linear coefficient of thermal expansion | 导热系数 | JISR2618 | 0.2 W/m/K |
| Heat distortion temperature | 0.45MPa未退火，HDT | ASTM D648 | 230 °C |