PA66/6 9AB23500 H 4Plas
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 70.0 MPa |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2/5 | 3500 MPa |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 70.0 MPa |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| other | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| UL flame retardant rating | 1.60 mm | UL 94 | V-0 |
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 850 °C |
| flammability | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.5 % |
| Shrinkage rate | MD | 1.2 % | |
| water content | ISO 960 | <2000 ppm | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.5 % |
| density | ISO 1183 | 1.16 g/cm³ | |
| Shrinkage rate | TD | 1.2 % |
| Thermal performance | Test Condition | Test Method | 4Plas/ 9AB23500 H |
|---|---|---|---|
| melting temperature | ISO 11357 | 245 °C |