PA6 235L TYNE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TYNE USA/235L |
|---|---|---|---|
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 59 J/m |
| hardness | Test Condition | Test Method | TYNE USA/235L |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | TYNE USA/235L |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 80 % |
| tensile strength | ASTM D638 | 75.8 MPa | |
| Flexural modulus | ASTM D790 | 2760 MPa | |
| bending strength | ASTM D790 | 110 MPa | |
| Impact strength of cantilever beam gap | 6.35mm | ASTM D256 | 59 J/m |
| physical property | Test Condition | Test Method | TYNE USA/235L |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 1.6 % |
| Rockwell hardness | R计秤 | ASTM D785 | 115 |
| density | ASTM D792 | 1.13 g/cm3 | |
| ASTM D792 | 1.13 g/cm³ | ||
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.0to1.4 % |
| 3.18mm | ASTM D955 | 1.0-1.4 % |
| Thermal performance | Test Condition | Test Method | TYNE USA/235L |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 60.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 177 °C | |
| 1.8MPa,未退火，HDT | ASTM D648 | 60.0 ℃ | |
| 0.45MPa,未退火，HDT | ASTM D648 | 177 ℃ |