PC/ABS CX7240U-7M10001 SABIC INNOVATIVE SINGAPHORE
CYCOLOY™
Electrical field、Electronic field、Architectural application、Outdoor applications、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Aerospace Applications、Liquid handling
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2950 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 65.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 100 % |
| 断裂 | ISO 527-2/50 | 90 % | |
| Flexural modulus | --5 | ISO 178 | 2500 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 104 Mpa |
| --5,6 | ISO 178 | 96.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2750 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| 屈服3 | ASTM D638 | 4.1 % | |
| tensile strength | 断裂3 | ASTM D638 | 58.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2530 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| 0.60 mm | UL 94 | V-1 | |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| 0.40 mm | UL 94 | V-2 | |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Melt volume flow rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| melt mass-flow rate | 260°C/2.16 kg | ASTM D1238 | 16 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.20 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 6.3E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 5.4E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 100 °C |
| RTI | UL 746 | 90.0 °C | |
| vicat | -- | ISO 306/B120 | 113 °C |
| -- | ASTM D152510 | 106 °C | |
| ball-indentation hardness | 73 到 77°C | IEC 60695-10-2 | 通过 |
| vicat | -- | ISO 306/B50 | 110 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ISO 11359-2 | 6.2E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 99.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDT | ISO 75-2/Af | 93.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 5.4E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 89.0 °C |
| RTI Elec | UL 746 | 90.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/CX7240U-7M10001 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Processing (melt) temperature | 270 to 300 °C | ||
| drying temperature | 90 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 4.0 hr | ||
| Temperature in the middle of the barrel | 260 to 300 °C | ||
| Temperature at the rear of the barrel | 260 to 300 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the front of the material cylinder | 265 to 300 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 265 to 300 °C |